How to select a Chinese injection mold supplier?Date of Release:2021-06-13 Click：101
The major reason that American and European companies source plastic injection molds in China is price, at the end of the day that is the major factor. However if we want to have a feel good discussion and ask what to look for when selecting a Chinese injection mold supplier we can look for the following:
References -- Get it from them and do your homework
Origin of Tool Steel
Capital investment in shop and equipment -- Is it a dive?
In place (established method) project plan that shows every aspect of build and give updates
Knowledge of your product -- Have they done this before?
How much capability do they have -- Can they do everything in-house?
Capacity and what is it at the moment you are placing your P.O.
Are they able to service you globally?
Injection mold manufacturing is a very complicated process, from the steps of initial design, processing, assembly, mold trial, etc. to the final mass production. During the entire life cycle, we must take into account effects of each manufacturing process on the quality of injection mold. And concern every detail to improve the quality of injection mold.
With injection molding and machine using both are indispensable. The operation of mold injection is actually accomplished by operating the injection molding machine. The correct use and maintenance of the mold is an important factor in ensuring the continuous production of high quality plastic products and extending the life of the mold injection molding. Using and carefully maintaining injection molding correctly is of great importance to maintaining normal production and improving company benefits. Then pay attention to several aspects.
Reliable injection molding manufacturers in China
How to choose reliable injection molding manufacturers?
This question is believed to be of concern to many companies. A reliable injection molder supplier is not only a guarantee of product quality but also a solid backing for product production cycle and stability. Therefore, most companies will have a relatively long inspection period when they choose an injection mold factory. How can one judge the selection of such a company?
Mold trail refers to, in the product development and manufacturing, the test injection step that is carried out after the mold making is completed and before the mass production.
In order to avoid unnecessary waste of time and trouble, it is indeed necessary to pay patience to adjust and control various processing conditions, and to find the best temperature and pressure conditions, and to formulate standard test procedures, which can be used to establish Daily work methods.
Record and analyze data which is used for the need of modifying molds and production conditions, and providing reference for future volume production.
At present, the mold temperature is often neglected during the test of the mold, and the mold temperature is the least easy to grasp in the short-term mold test and future mass production. The incorrect mold temperature can affect the size, brightness, shrinkage, rhythm and under-charging of the sample. If you do not use a mold temperature controller to grasp, the difficulties will occur in the future’s mass production.
Introduce the mold quality effect factors , the basic ways of mold quality improving, and typical cases in using right methold and maintenance.
Even if is very professional and have rich experience in plastic mold processing, also can't guarantee the production of plastic is one hundred percent qualified, more or less has some processing defects. But these defects can be controlled and life of the mold can be improved.
Considerations of outsourcing injection mold to China
If you plan to make molds outside of the United States, and you don't have an international patent. Remember you have no legal means of stopping someone in China from building a second set of injection molds and producing your product and selling it in say Australia, Japan or Europe, quite possibly before you roll it out in the United States.
A lot of problems come from communication and working habits from my experience actually. Many injection mold manufacturers in China can't speak and listen English very well, it may be the biggest reason of causing some problems. If communication no problem, Chinese manufacturers are very much willing to do everything possible for their customers.
The reasons of warpage in injection molding
Warpage is usually caused by molded-in stresses. The issue of warpage is related to being a semi crystalline material, HDPE, being semi crystalline polymer, will have differential shrinkage along and across the flow leading to warpage. It is difficult to eliminate this problem just by optimizing processing parameter. If use of multiple gates is possible, that might help multidirectional flow leading to lesser warpage.
The two areas that will have greatest affect are injection mold temperature and gating being both location and type. Not knowing configuration or flow difficult to give specific advice, but think of the part on a molecular scale. Imagine the surface of part being interconnected crystals with cooling starting at coldest surface of injection mold which will be multiple points and spreading out in a circular shape all within fractions of a second. You want the coldest surface possible and repeatable and a flow front that fills mold as evenly as possible. The more even the flow front in relation to part configuration from one side across to other and a plastic injection mold surface temperature that is a uniform temperature will minimize warp. There are some design tricks that would also minimize warpage but you may past that point. As to type of gate, as large as possible so you are not adding heat through shear. Also monitor melt temp at nozzle, looking for lowest temp that will enable complete mold fill.
I was an injection molding trouble shooter for eight years, and in my job today I come across good and bad ones all the time. You can see very quickly which is which I have seen a lot of articles about taking people with boat loads of experience, in principal I would agree, but be cautious that the experience is not blinding the person to think they know it all.
Injection molding troubleshooter
The big part missed is a good communicator. The problem being an injection molding trouble shooter is you can be called in to solve a problem and by fixing it the people originally working on can be put out joint, the trouble shooter can be seen as critic of their work quality. So the best injection molding troubleshooting expert is someone who can work with the people to solve the problem and not need to be seen as the hero taking limelight.
How to minimize sink marks of injection molded parts?
Minimizing of sink marks can be achieved by following proper part design. The sink marks will not be eliminated if you have any ribs or structural features behind the 'A' surface. But with proper part design they can be minimized to a point that they are not visible.
You will never cover sink marks up with the paint, they will appear worse than they do on the plastic part. There are a few good way to check for sink on a part before painting. these are:
Project a grid pattern of bright lines on the part, using an overhead projector, distortion in the grid pattern shows sinks easily.
Wipe the part with Alcohol and observe the drying pattern. Sink areas take longer to dry.
How to Increase/Decrease Injection Molding Shrinkage?
Injection molding processing can affect shrinkage, but not as much as fillers.
Increase shrinkage: shorter cooling time in injection mold. Higher mold temperature. Greater product thickness. Higher resin melt temperature during injection. More plasticizer in resin. Less injection speed. Lesser packing / holding pressure and volume.
Decrease shrinkage: longer cooling time in the injection mold. Lower mold temperature. Thinner product walls. Lower resin melt temperature during injection. Greater injection speed. Greater packing / holding pressure and volume. Fillers such at talc, glass beads, or glass fibers (more anisotropic shrinkage with fibers).
Injection rates, packing, and mold temperatures can significantly affect molded-in stress or allow voids and sink marks. Molded-in stress can affect warp, solvent sensitivity, dimensional stability, and impact resistance; so, these tertiary effects need to be considered.
Injection mold technologies seminars may help mold companies to educate their people. But I think that each injection mold shrinkage problem you face in real life is caused by too many effects that one rarely can keep track of it.
One thing you always should keep an eye on is the crystallization of materials which is responsible for the biggest part of the shrinkage. And this crystallization is not just influenced by the process (PVT- is one head point).
But also by the limitations made by the machine and the injection mold (cooling time-->crystallization rate).
Also the fillers in a material can have so much influence on crystallization.
Also keep in mind that post process shrinkage also causes crystallization and thus injection mold shrinkage.
Not every part has uniform wall thickness, this will cause ununiformed shrinkage occurs.
Also so-called amorphous thermoplastics are not 100 % amorphous und thus can shrink depending on the overall conditions named above.
How to choose mold flow software, Autodesk or Moldex?
Both are highly developed and very capable products. Either one is much, much better than no process calculation at all. In that sense, you can’t go wrong whichever one you choose. That’s just as well, because it is going to be difficult to answer the question in a truly informed manner. There can be few if any people who are equally fluent and experienced in both systems, under industrial conditions.
A niche product such as injection molding process simulation needs support by industry experts who can hold their own on the factory floor as well as at the keyboard. I think Autodesk’s CAD reseller channel struggles to deliver that. I am just an onlooker now, but I get the sense that Moldflow has stalled, and all the momentum is with Moldex. Certainly, over the last few years, I have read and seen quite a lot about Moldex and almost nothing about Moldflow. It is just a niche for Autodesk but it’s core business for Moldex.
Injection Mold Venting Problem
Venting can be one of the most important parts of an injection molded product. Many engineering materials like PBT (Polybutylene terephthalate) have a tendency of out-gassing. The best practices that I have to date are:
Add 10mm wide vents spaced 30mm from each other all the way around parting line.
Always follow the recommendations of the material company for vent depth.
If the product has a 50mm or larger core out the injection mold must be vented through the ejector plate, which means that you must drill through the core side (without hitting any water lines etc.) I usually use a 5mm or 1/4" drill bit to do so.
Always vent to atmosphere.
Polish the vents and vent channels. This makes the vent self-cleaning. It also allows the gases to escape much better.
A really old trick to ascertain whether the injection mold has an inherent venting problem or not, and this trick is somewhat dependent upon injection mold construction so must be evaluated as applicable on a case by case basis (more about this at the end) is to use shipping tape, or masking tape, depending upon the gap desired laid across the injection mold major parting line to artificially "spread" the mold and create a vent gap. Evaluate the fill in the taped v non taped shots without making changes to the injection molding process settings.
Over the years we have been taken advantages of with the low cost of plastic injection mold manufacturing in China. You get what you pay for. I have heard of an injection mold cracking in half just last year from China, water poring out of it in the press. As an injection mold maker back in the 80's and 90's we started to see import steel making its way to our machines. We could tell on the CNC's or polishing we were not getting what we bargained for. After heat treat OMG, warp. We use to say they put old "bed springs" in the alloy mix. When drilling a hole in this steel it would not be constant feed rate by hand, you could feel the drill push easy then hard etc. So we had to be very precise in ordering our plastic injection molds with certification. We ordered 4 large injection molds from a Chinese manufacturer in 2004, the heat treat was horrible, we did not get our certification, it looked fake. Someone was trying to pull a fast one. I hardness tested several blocks from the plastic injection molds, not good. We spent approx $450,000 for those injection molds back in 2004 and we tried to outsource and handle the engineering real close. We tried to do everything real and it back fired. These injection molds were for electrical components and tolerances on my parts were critical, 4 to 8 cavity molds, the quality was just not there. Glass filled nylon wore down these plastic injection mold in 8 months, we had to retool.
Chinese injection molds cut major corners on water, mold steels, unless you really get after them to use good mold steels. I have seen Chinese plastic injection molds that literally warp in the press because their injection molds are the softness of lead. I have seen well-made Chinese molds, but again, the materials used have been sub-par. The delay in communications is also an ongoing problem. That's one reason I use America, UK or Italy over China -- never have to worry about any of the things previously mentioned. The only reason that Chinese injection molds remain more competitively priced is the fact that the country pegs its currency to the dollar, so you never see the true cost. In the near future, the Chinese will not be able to continue pegging their currency to US dollar especially when the dollar is getting trashed by our own government. Because of this weak dollar policy, it makes everyone except China very expensive. Yet, for our European friends, it makes US made stuff cost competitive. However, even with our virtually worthless currency, I still get 25-30% less costly tooling in Portugal.